| MOQ: | 500 kg |
| Standard Packaging: | PE wrap + bubble film + processed wooden pallet |
| Delivery Period: | within 10 days |
| Supply Capacity: | 10000 kg per week |
| Test Item | Test Method | Unit | Value |
|---|---|---|---|
| Density | GB/T 6343 | g/cm³ | ≤0.7 |
| Thickness | GB/T10003-2008 5-05 | μm | 30 ±5% |
| Width | mm | 1000 ±2% | |
| Whiteness | GB/T 2913 | % | ≥88 |
| Tensile Strength (MD) | GB/T 1040.3-06 | MPa | ≥75 |
| Tensile Strength (TD) | GB/T 1040.3-06 | MPa | ≥140 |
| Fracture Nominal Strain (MD) | GB/T 1040.3-06 | % | ≤160 |
| Fracture Nominal Strain (TD) | GB/T 1040.3-06 | % | ≤60 |
| Heat Shrinkage (MD) | GB/T 10003-2008 | % | ≤4.0 |
| Heat Shrinkage (TD) | GB/T 10003-2008 | % | ≤2.0 |
| Haze | GB/T 2410-2008 | % | ≤48 |
| Friction Coefficient (Treated Side) | GB/T 10006-88 | uN | ≥0.25, ≤0.4 |
| Friction Coefficient (Non-Treated Side) | GB/T 10006-88 | uN | ≤0.45 |
| Wetting Tension | GB/T 14216-2008 | mN/m | ≥38 |
| Heat Sealing Strength | GB/T 10003-2008 | N/15mm | ≥2.0 |
| MOQ: | 500 kg |
| Standard Packaging: | PE wrap + bubble film + processed wooden pallet |
| Delivery Period: | within 10 days |
| Supply Capacity: | 10000 kg per week |
| Test Item | Test Method | Unit | Value |
|---|---|---|---|
| Density | GB/T 6343 | g/cm³ | ≤0.7 |
| Thickness | GB/T10003-2008 5-05 | μm | 30 ±5% |
| Width | mm | 1000 ±2% | |
| Whiteness | GB/T 2913 | % | ≥88 |
| Tensile Strength (MD) | GB/T 1040.3-06 | MPa | ≥75 |
| Tensile Strength (TD) | GB/T 1040.3-06 | MPa | ≥140 |
| Fracture Nominal Strain (MD) | GB/T 1040.3-06 | % | ≤160 |
| Fracture Nominal Strain (TD) | GB/T 1040.3-06 | % | ≤60 |
| Heat Shrinkage (MD) | GB/T 10003-2008 | % | ≤4.0 |
| Heat Shrinkage (TD) | GB/T 10003-2008 | % | ≤2.0 |
| Haze | GB/T 2410-2008 | % | ≤48 |
| Friction Coefficient (Treated Side) | GB/T 10006-88 | uN | ≥0.25, ≤0.4 |
| Friction Coefficient (Non-Treated Side) | GB/T 10006-88 | uN | ≤0.45 |
| Wetting Tension | GB/T 14216-2008 | mN/m | ≥38 |
| Heat Sealing Strength | GB/T 10003-2008 | N/15mm | ≥2.0 |